Nano PVDF Panels uses a new and exciting technology to change the molecular structure of the surface of the paint. This improves and enhances the paint coating by giving it a longer color and gloss retention. It is applied as a 4th layer of coating over and above the 3rd layer of PVDF coating. The 4th layer of Nano coating which is made from a water soluble chemical seals any air gaps between the tiny paint molecules thus preventing dirt, water, permanent paint or any foreign particles to penetrate through the paint surface, making the paint surface lipophobic and hydrophobic.
The high-tech Nano technology, it has more super advantages in pollution resistance, self-cleaning function, acid resistance and alkaline resistance.

Aluminum Alloy	AA1100, AA3003
Aluminum skin	0.21mm,0.30mm,0.35mm,0.40mm,0.45mm,0.5mm
Panel thickness	3mm,4mm,5mm,6mm
Panel width	1220mm,1250mm,1500mm
Panel length	2440mm,3050mm,4050mm
Surface treatment	NANO PVDF
Colors	AluEastbond Color chart, customized color available
Customers size	accepted
GLOSSY	30%-50%

Tolerance:

Panel width: ±2mm Panel length:±3mm

Panel thickness: ±0.2mm Panel diagonal: ≤5mm

Aluminum sheet thickness: ±0.01mm

Excellent easy-cleaning
Pollution resistance
Oil resistance
Good friction resistance
Strong acid & alkali resistance
Outstanding weather resistance

1. Wall curtain, Cladding and Facade

2. Hotels and commercial mansions

3. Exterior renovation for old buildings

4. Subway and airports

5. Industry plants and materials,

6. Vehicle and boat materials

Description	Test standard	NANO PVDF
Thickness of coating	PVDF paint≧25um	35um to 37um
Coating flexibility (T-bend)	PVDF paint≥2T	2T
Color different	ΔE≦2.0(follow color sample)	ΔE<2.0
Pencil hardness	≧HB	5H
Chemical resistance	5%HCI or 5% NaOH test in 24 hours -No change;ASTM D1308	No change
Coating adhesion	ISO 15184:1998 Section 6	The edges of the cut are completely smooth,none of the square of the lattice is detached.
Resist solvent	No change for 200 times(MEK)	No change
Boiling water resistance	EN438-2:2005 Section 12	Rating 5,no visible change.Average change of mass: 0.08%;Average change of thickness:1.36%
Peeling strength/stripping strength	BS EN319:1993	2.4N/mm2
Impact test for paint	ISO6272-1:2002 Section 8	The coating not crack or peel after 2kg weight ball dropped from 1.5m height
Abrasion resistance (L/Mil)	ISO7784-2:1997 Section 8	The abrasive rubber wheel: Taber H-22; the cycles number:100; the mean loss mass:91mg
Temperature resistance	EN438-2:2005 Section 19	Rating 4, change of gloss only
Coefficient of linear Thermal Expansion	ISO11359-2;1999 Section 7	1.3×10-4K
Detergent resistance (3%)	ASTM D2248	No change
Humidity Resistance (3000hrs,100%RH,100°F)	ASTM D2247	No change
Salt spray resistance (3000hrs,5% salt)	ASTM B117	No change
Resistance to Staining	EN438-2:2005 Section 26	Rating 5,no visible change